1. INTRODUCTION :

YE-6683 is a indoor saturated carboxylic polyester resin curing with epoxy resin at 60/40 for

thermosetting powder coating with excellent flow, applied to indoor decorative and functional

painting. Better flow than YE-6682.

2. CHARACTERISTICS OF THE RESIN

Appearance…………………….pale granules

Acid value (mg KOH/g)…………………48-57        (1)

Color………………………………….max.2        (2)

Viscosity at 165°C(mPa...S)……… 6000--13000        (3)

Glass transition temperature(Tg) .    approx.56°C      (4)

Softening point(°C)…………………… 96-102

(1)ISO-3682                          (2)ASTM-D-2849

(3)ICI CONE & PLATE        (4)DSC(METTLER)

3. APPLICATION:

TYPICAL POWDER FORMULA:  

Barium sulfate…………………………100      (1)

Titanium dioxide………………………. 300     (2)

Polyester YE-6683………………………. 360   

Epoxy   .………………………………... 240       (3)

Flow control agent……………………….. 10      (4)

Benzoin ………………………………….5

(1) Shaanxi Fuhua Chemical Co., Ltd

(2) DuPont R-902 or R706

(3)ARADITE GT-7004 WPE:775 (Supplier: Ciba-Geigy)   

D.E.R.663UWPE:780 (Supplier: DOWS Chemical) Others epoxy suppliers are also suitable.       

YE-6683/EPOXY =60/40

(4) YL-1080 (Silica Adsorption 65% Supplied by Yin Yang Resin Co., Ltd)

4.MANUFACTURING PROCEDURE AND TESTING 

MANUFACTURING  

a.  Pre-mixing ( dry blend of the above components)

b.  Homogeneous extrude at temperature of 105°C-115°C   

c.  Cool down and early pieces   

d.  microized to obtain a fine free -flowing powder maximum particle size of 80µm

COATING CONDITION:

  Voltage……………………………60-80kv

  Air pressure………………………1-2kg/cm2

  Test panel……………………….0.35 mm steel panels

CURING CONDITION: 

10 minutes at 200°C (object temperature)

TEST RESULT:

Film thickness………………………60-80mm

Gloss………………………………>90% (1)

Erichsen slow penetration………... >7mm (2)

Direct/reverse impact……………… >50kg-cm (3)

Conical mandrel……………….    pass (4)

Crosshatch adhesion…………...……Gt=0 (5)

(1)ASTM D-523(60°)          (2)DIN 53165

(3)ASTMD-2194                  (4)ASTM D-522

(5)DIN53151

5. PACKING AND STORAGE

25 kilogram paper bag or PE bag; Stored in a cool dry indoor place at temperature of   

-20°C－35°C, Avoid long-term exposure to direct sunlight. In the above-mentioned storage

conditions the shelf life of resins for 1 year. Experience has shown that the storage life of the

resin up to 3 years, it is proposed that the testing products beyond the shelf-life products can still

be used for qualified.

The above-mentioned indications are based on carefully made tests. No liability can be assumed

in the event of any inaccuracy or incompleteness being found in the value listed above and

consequently we recommend evaluation in your own laboratories prior to use.