1. INTRODUCTION

  YE- 9500 is a indoor saturated carboxylic polyester resin compounding with epoxy

resin at 75/25 for thermosetting matting powder coating, applied to indoor decorative

and functional powder coating.

2. CHARACTERISTICS OF THE RESIN

   Appearance…………………………pale granules

   Acid Value (mg KOH/g)……………20-26        (1)

   Color………………………………max.2         (2)

   Viscosity at 165℃ (mPa…S)……30000-45000    (3)

   Glass Transition Temperature (Tg)…approx. 57ºC (4)

   Softening Point (℃)………………105-115

(1)ISO-3682

(3)ICI CONE & PLATE

(2)ASTM-D-2849

(4)DSC(METTLER)

3. TYPICAL POWDER FORMULA                  A              B: 

Barium Sulfate………………………………200          200    (1)

Titanium Dioxide……………………………200          200    (2)

Polyester YE-9500………………………… 450          150    

Epoxy……………………………………… 150          450     (3)

Flow Control Agent…………………………10           10     (4)

Benzoin……………………………………  5            5

603-1A……………………………………      ---           40

(1) Shanxi Fuhua Chemical Co., Ltd

(2) Dupont R-902

(3) ARALDITE GT-7004, WPE: 775 (Supplier: Ciba-Geigy)

    D.E.R.663U WPE: 780 (Supplier: DOWS Chemical) other epoxy supplier are also

suitable. YE-9500/EPOXY = 75/25

(4)YL-1080     (Silica Absorption 65% supplied by YinYang Resin Co., Ltd) 

4. MANUFACTURING PROCEDURE AND TESTING

（1） MANUFACTURING

a. Pre-mixing (dry-blend of the component above)

b. Homogeneous extrude at temperature of 110-115°C)

c. Cool down and initial grinding

d. Milling and sieve to obtain a fine free-flowing powder maximum particle size of

80 µm

（2）COATING CONDITION:

Voltage………………………… 60-80 kv

Air Pressure……………………1-2kg/cm2

Test Panel………………………0.35mm steel panel

（3） CURING CONDITION:  

10 minute at 200°C (object temperature)

（4）  TEST RESULT                    A                   B:   

Thickness………………60-80Filmµm       60-80µm

Gloss………………………>88%              <10

Conical Mandrel……………Pass                 Pass  

Hardness……………………HB-H                HB-H

5. PACKING AND STORAGE

25 kilogram paper bag or PE bag; stored in a cool dry indoor place at temperature of

-20℃ to 35℃. Avoid long-term exposure to direct sunlight. The shelf life of the resin is

one year in the above-mentioned storage conditions. Experience has shown that storage

life of the resin is up to 3 years. It is proposed that the testing product beyond the shelf life

can still be used after tested qualified.  

Note: The above-mentioned indications are based on carefully made tests. No

liability can be assumed in the event of any inaccuracy or incompleteness being found in

the value listed above and consequently we recommend evaluation in your own

laboratories prior to use.